6061 aluminum plate for aircraft

La description

6061 Plaque d'aluminium Manufacturer RAYWELL MFG supply aluminum-silicon-magnesium alloy, strengthened by precipitation hardening. This alloy has medium strength, formabilité, soudabilité, usinabilité et de résistance à la corrosion.

Plaque d'aluminium 6061 T6 temper has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). In thicknesses of 0.250 pouce (6.35 mm) or less, it has elongation of 8% ou plus; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties.

Alliage 6061 alumium plate has a relatively high strength, easily welded and is widely used not only for making bicycle frames, but also in construction, avion, shipbuilding.

Les principaux éléments d'alliage dans 6061 plaque d'aluminium are magnesium and silicon, avec une force modérée, bonne résistance à la corrosion, weldability and oxidation effect. Widely used in various industrial structures requiring certain strength and high antibiotic corrosion resistance.

The main chemical components are: cuivre 0.15-0.4%, silicium 0.4-0.8%, le fer 0.7%, manganèse 0.15%, magnésium 0.8-1.2%, zinc 0.25%, chrome 0.04-0.35%, titane 0.15%.

The difference between 6061 plaque d'aluminium T6 and T651 is that, under normal circumstances, the internal stress of T6 will be relatively large, and it will be deformed during processing. The most suitable state for processing should be T651, stretched on the basis of T6, and eliminate internal stress.

6061-T6 : cooling after solution heat treatment to achieve high strength, no cold working;

6061-T651 : Cooling after solution heat treatment to achieve high strength, and then cold stretching by stretching machine to eliminate residual internal stress after heat treatment, so as to ensure the precision of machined products without deformation after deep processing.

6061 T6 Aluminium Plate is a commonly used aluminum alloy. Unless otherwise specified, it is generally in the 6061 T6, et 6061 T651 is the best feature of the 6-series aluminum alloy, and it is a fighter in the 6000-series aluminium alliage. It has excellent processing performance, excellent welding characteristics and electroplating performance, bonne résistance à la corrosion, high toughness, no deformation after processing, dense material without defects, easy polishing, easy coloring and film formation and excellent oxidation effect.

Since 6061-T651 is a high-quality aluminum alloy product produced by heat treatment and pre-stretching process, although its strength cannot be compared with 2XXX series or 7XXX series, it has many characteristics of magnesium and silicon alloys, excellent processing performance and excellent welding Features and electroplating, bonne résistance à la corrosion, haute ténacité et aucune déformation après traitement, compact material without defects and east to polish, film facile à colorier, excellent effet d'oxydation et autres excellentes caractéristiques. The representative applications of 6061-T651 include aerospace fixtures, electrical fixtures, and communication fields, and are also widely used in automated mechanical parts, precision machining, mold manufacturing, electronics and precision instruments, SMT, PC board solder carriers, etc.