Aluminum closure sheet coil is a type of aluminum coil that is specifically designed for manufacturing bottle caps and closures.

Aluminum closure sheet coil is typically made from high-quality aluminum alloy and has a smooth surface finish to ensure proper sealing of the bottle.

The Aluminum closure sheet coil is usually produced in various thicknesses and widths to meet the specific requirements of closure manufacturers.

铝盖卷材广泛应用于饮料行业，用于密封各种尺寸和形状的瓶子.

该 3105 H14 aluminum closure sheet coil is a high-quality 铝 通常用于生产瓶子和罐头等容器的密封盖的合金.

H14 状态名称表示铝已经过应变硬化和部分退火, 使其适用于成型和深拉应用.

This aluminum closure sheet coil is known for its excellent corrosion resistance, 成形性, 和可焊性, 使其成为食品和饮料行业的理想选择.

它也很轻且可回收, 使其成为包装应用的可持续选择.

全面的, 该 3105 H14 铝 封闭片卷材是一种多功能且可靠的材料，可满足封闭盖制造的严格要求.

8011 H14 aluminum closure sheet coil is a type of aluminum alloy coil that is specifically designed for making closures for various packaging applications.

H14 名称表示铝合金经过了应变硬化过程, 这增加了其强度和耐用性.

This type of aluminum closure sheet coil is commonly used in the production of bottle caps, 罐盖, 以及其他类型的食品和饮料容器封盖.

铝封闭板卷材具有高度耐腐蚀性, 轻的, 并且易于使用, 使其成为需要紧密密封的包装应用的理想选择.

8011 H14铝封闭片卷材是一种用途广泛且可靠的材料，以其优异的性能和性能广泛应用于包装行业.

Aluminum lid roll from Aluminum closure sheet coil is a metal lid that is commonly used to package and seal various products such as cosmetics, 食物, 药品, 等等.

铝封板卷材生产的铝盖卷具有以下特点:

材质优良: 铝盖卷一般由以下材料制成 铝 合金材料, 具有良好的耐腐蚀性和抗氧化性，能有效保护产品免受外界环境的影响.

密封性能好: 铝盖卷具有优良的密封性能, 可有效防止产品泄漏和污染，确保产品质量和安全.

美丽优雅: 铝盖卷外观整齐、美观, 可以提升产品的整体档次和附加值.

便于使用: 铝盖卷的安装和拆卸非常方便, 可以大大提高生产效率，降低人工成本.

铝盖卷广泛应用于各个包装领域, 尤其是在化妆品领域, 食物, 制药及其他行业.

随着人们对产品质量和安全的要求不断提高, 铝包覆卷的应用将会越来越广泛.

与之比较 8011 铝封闭片卷材, 3105 H14 H16 铝封板有足够的强度, 所以它的强度足以承受气体压力.

3105 H14 / H16铝盖卷材广泛用于制作碳酸饮料、矿泉水的旋盖.

我们可以治疗 3105 带磷酸铬酸盐和 DOS 涂层的铝制封闭板卷, 在我们的普通纸的基础上印上不同的颜色.

瑞意铝业 / RAYIWELL MFG是中国最大的铝封闭板卷供应商, 针对各种瓶盖需求有完整的解决方案, 例如铝制螺旋盖, 罗普管帽, 小瓶密封件, 所有章节, 拧开盖子, EOE终端和化妆品包装.

作为一家铝封闭板卷材公司, 我们很荣幸能与 Guala Coloseres 等知名合作伙伴合作, 日本彩色, CSI 颜色, 硬化, 马拉色彩, 和 Federfin 技术.

Aluminum Closure Sheet Coil

闭包 (帽子) 是封闭各种类型容器的物品. Aluminum closure sheet coil are used to produce Closure that seal a wide variety of glass bottles and bottle cans for soft drinks, 营养饮料等.

We provide Aluminum closure sheet coil materials to meet customer needs for closures that protect a container’s contents, 打开轻松，非常方便.

3105 螺旋盖用铝封闭片卷

我们可以治疗 3105 磷酸铬酸盐铝螺旋盖板, 和 DOS 涂层, 印有不同的颜色, 在我们的普通纸的基础上.

我们控制材料成分, 滚压温度和时间,和退火温度以生产最佳材料，以满足客户的性能需求, 比如它的开通能力和成耳率.

凭借我们良好的平整度和方形度, 我们可以防止色隙, 打印时出现不均匀或打印错位.

Surface type of Aluminum closure sheet coil:
一个. 普通轧光铝带;
b. DOS 油润滑表面处理;
C. 镀铬表面处理;
d. 一侧金色/白色/红色/蓝色/黑色,等其他颜色, 另一面涂有防护漆;
Ë. 两面清漆/透明漆;

铝封闭板卷的回火及力学性能

8011 PP帽用铝封闭片卷, 罗普帽, 旋开帽, 接线片盖

铝封闭板的最大品质是可拉伸性和漆附着力, 保证图纸和设计的最高质量印刷.

瑞威尔 / 瑞亿铝业生产一系列优质合金和状态材料，适用于各种瓶盖应用, 从酒中, 烈酒和软饮料到药品包装.

RAYIWELL 供应用于制造瓶盖的铝盖板卷. 应用范围从威士忌和其他饮料瓶的螺旋盖到酒瓶的铝盖.

铝 – 生产瓶盖的理想材料:

 

Surface type of Aluminum closure sheet coil:
一个. 普通轧光铝带
b. DOS 油润滑表面处理
C. 镀铬表面处理
d. 一侧金色/白色/红色/蓝色/黑色,等其他颜色, 另一面涂有防护漆
Ë. 两面清漆/透明漆

测试项目: 高压灭菌测试, 汞测试
抗拉强度: 130-155兆帕
伸长: 2.5-3.5%
耳环: 2% 最大限度
包装: 出口标准木箱;

Application of Aluminum closure sheet coil :
罗普帽, PP帽, 卷装防盗盖, 铝制防盗盖, 防盗封口, 铝瓶盖, 铝制螺旋盖, 撕下盖子, 掀掉盖子.

5052 Aluminum closure sheet coil for Ring Pull Can Lid

1. Typical Products
5052 aluminum ring pull can lid strip: 厚度: 0.22 – 0.5mm; 宽度: 1280毫米; 5052/5182: H19 alloy

2, Product Features
(1) Ring Pull stock generally adopts 5182 aluminum alloy processing, the Ring Pull Can Lid material generally use 5052 和 5182 aluminum alloys processed;
(2) flexible, stamping deformation is not easy to crack;
(3) small density, 轻的, smooth surface, 感觉不错;
(4) 环保易于回收再利用.

3. 主要质量要求
表面处理良好, 不允许有黑色, 分数, 轮胎痕迹, 腐蚀, 压力褶皱, 折痕, 矫直滚筒印刷, 油污, 棍棒伤害, 划痕, 金属和非金属压制成等. 明显缺陷, 带钢平整度大于10I (或波高小于或等于 3 毫米, 波长最好大于400mm).

4. 产品控制
(1) 严格控制良好的宽度公差.
厚度公差: + 0.01毫米 (优选0.005mm)
宽度公差: + 1毫米
平整度要求: 高度小于3mm, 之内 1 米的波数小于 3;
(2). 机械性能:
屈服强度: 295-380MPA;
抗拉强度: 355-420 MPA;
延伸率: 5.5%;
烘烤后: 屈服强度: 320兆帕; 抗拉强度: 360MPa以上; 伸长率: = 5.5%
(3). 板形控制:
与卷相结合, 弯曲辊, 喷涂使用控制好平整度, 确保热机凸度控制在 0.1 〜 0.8%, 网络火热视觉无明显波动.
(4). 外观质量:
端边无裂纹, 卷端整齐, 无交错金字塔.

5. 铸造工艺控制点
(1) 控制Na的含量, 以避免钠含量过高, 钠脆化的出现 (记忆可能与纳粹有关);
(2) 注意添加气体, 精制, 防止后续轧制产生大裂纹、裂纹;
(3) 注意除炉渣初始气体等冶金质量, 防止客户使用爆炸罐时造成的炉渣.

6. 热轧工艺
(1) 热轧机工艺流程: 大型单面铣15-20mm, 侧面铣10-15mm;

(2) 加热系统: 炉气温度 490 度, 33 保温时间, 烘烤温度 475-485;

(3) 滚轮式: -0.02毫米;

(4) 乳化指数: 根据热轧时的实际生产情况;

(5) 机器下厚度: 满足6.0-6.5mm之间的工艺要求, 尽量由下限控制;

(6) 表面控制: 平坦道路上的热表面, 第一卷和第二卷可以有均匀的白化现象, 最终线圈通过亚表面暴露出金属光泽和颜色均匀, 无发白及粘铝现象.

表面不允许有划痕, 擦伤, 沙洞, 等等缺陷的深度, 可以带有低碳钢的印记, 轻度沙眼, 轻微点蚀, 在皮边重量范围内可切边.

(7) 平整度控制: 带卷, 弯曲辊, 喷涂使用控制好平整度, 确保热机 8 冠控制之间 0.1 〜 0.8%, 网络火热视觉无明显波动.

(8) 外观质量: 边缘裂纹端面, 辊面整齐, 无交错金字塔.

通过工厂技术及科研部门, 不懈努力, 瑞艺铝盖库存, 拉环库存产量已达到 4000 吨.

卓越的产品质量和良好的售后服务, 赢得了国内外用户的一致好评.

5182 Aluminum Strip Coil for Ring Pul

1. Typical Products

5182 aluminum ring pull strip: 厚度: 0.25: 0.5毫米; 宽度: 1280毫米; alloy temper: 5182 H19

2, Product Features

(1) Ring Pull stock generally adopts 5182 aluminum alloy processing, the Ring Pull Can Lid material generally use 5052 和 5182 aluminum alloys processed;

(2) flexible, stamping deformation is not easy to crack;

(3) small density, 轻的, smooth surface, 感觉不错;

(4) 环保易于回收再利用.

3. 主要质量要求

表面处理良好, 不允许有黑色, 分数, 轮胎痕迹, 腐蚀, 压力褶皱, 折痕, 矫直滚筒印刷, 油污, 棍棒伤害, 划痕, 金属和非金属压制成等. 明显缺陷, 带钢平整度大于10I (或波高小于或等于 3 毫米, 波长最好大于400mm).

4. 产品控制

(1) 严格控制良好的宽度公差.
厚度公差: + 0.01毫米 (优选0.005mm)
宽度公差: + 1毫米
平整度要求: 高度小于3mm, 之内 1 米的波数小于 3;

(2). 机械性能:
屈服强度: 295-380MPA;
抗拉强度: 355-420 MPA;
延伸率: 5.5%;
烘烤后: 屈服强度: 320兆帕; 抗拉强度: 360MPa以上; 伸长率: = 5.5%

(3). 板形控制:
与卷相结合, 弯曲辊, 喷涂使用控制好平整度, 确保热机凸度控制在 0.1 〜 0.8%, 网络火热视觉无明显波动.

(4). 外观质量:
端边无裂纹, 卷端整齐, 无交错金字塔.

5. 铸造工艺控制点

(1) 控制Na的含量, 以避免钠含量过高, 钠脆化的出现 (记忆可能与纳粹有关);

(2) 注意添加气体, 精制, 防止后续轧制产生大裂纹、裂纹;

(3) 注意除炉渣初始气体等冶金质量, 防止客户使用爆炸罐时造成的炉渣.

6. 热轧工艺

(1) 热轧机工艺流程: 大型单面铣15-20mm, 侧面铣10-15mm;

(2) 加热系统: 炉气温度 490 度, 33 保温时间, 烘烤温度 475-485;

(3) 滚轮式: -0.02毫米;

(4) 乳化指数: 根据热轧时的实际生产情况;

(5) 机器下厚度: 满足6.0-6.5mm之间的工艺要求, 尽量由下限控制;

(6) 表面控制: 平坦道路上的热表面, 第一卷和第二卷可以有均匀的白化现象, 最终线圈通过亚表面暴露出金属光泽和颜色均匀, 无发白及粘铝现象.

表面不允许有划痕, 擦伤, 沙洞, 等等缺陷的深度, 可以带有低碳钢的印记, 轻度沙眼, 轻微点蚀, 在皮边重量范围内可切边.

(7) 平整度控制: 带卷, 弯曲辊, 喷涂使用控制好平整度, 确保热机 8 冠控制之间 0.1 〜 0.8%, 网络火热视觉无明显波动.

(8) 外观质量: 边缘裂纹端面, 辊面整齐, 无交错金字塔.

3004-O 灯头用铝合金带材

制作铝灯头, 先冲压后攻丝成螺旋状, 更薄的材料并能承受压力.

因此, 该 3004 灯头铝带需要具有高的机械强度和均匀的微观结构和深冲性能. 目前我们采用扁锭热轧生产3004-O铝合金带材压边圈.

为了使这个 3004 O铝合金带材, 我们必须控制材料的成分和铸轧工艺, 退火和最终退火过程的高温均匀性, 具有良好的深冲质量, 足够的力量, 良好的成型性能.

 

1070 化妆品瓶盖用铝带

瑞亿铝热轧品质使其适合深冲, 和 99.7% 高纯度让表面非常光亮, 而且表面非常柔软光滑.

总结 瑞亿铝业 1070 O 化妆品瓶盖非常适合用于香水瓶和化妆品瓶, 需要光亮的表面, 比如奶油罐, 香水瓶, 螺旋盖瓶, 化妆品帽等.

 

Clear lacquer Aluminum foil sheet for aluminium easy peel off end lid top

Aluminum is used as a substrate, generally with an organic coating on both sides. This is necessary to facilitate the forming of the metal and/or to protect the metal against corrosion during the shelf life of the can or can end.

Clear lacquer Aluminum foil sheet for aluminium easy peel off end lid top, which is Ideal materials for dry and non-processed foods, the main applications are the following :Milk Powder and Infant Formula,Instant Coffee and Tea, Snacks and Nuts, Non-food items.

Aluminium easy peel off end lid top for food cans are typically coated on aluminum sheets rather than coils.

Clear lacquer aluminum foil sheet for easy peel off foil end lid top coatings are applied by direct-roll coaters similar to those used in sheet coating operations for 3-piece can bodies, and some facilities use the same coating lines to coat can bodies and ends.

Clear lacquer Aluminum foil sheet Specification:

8011 H16/H14 Thickness 0.20–0.30mm, 宽度: 800mm —1000mm
长度: 800-1000毫米
包装: Wooden case, wooden pallet if request.

Clear lacquer Aluminum foil sheet Coating: 1. Both sides clear epoxy varnish 2. One side clear epoxy varnish, the other side color coated.

Clear lacquer Aluminum foil sheet Coating thickness:
Golden color /yellow color: both sides coating 5-6g/m2, one side coating 2-3g/m2.
White/red/black/blue color: Both sides coating 10-13g/m2.

Clear lacquer Aluminum foil sheet Coating quality:
Boiling Resistant: Boiling 121 degrees for half an hour, the paint does not fall off, do not change color.
Resistance to acetone and mercuric chloride: repeatedly wiping 20 times without significant stripping

8011 Lacquered Aluminum Strip for Flip Tear Off Seal Vial Cap

Aluminium flip tear off seal vial cap normally was made by 1060, and to be anodized so as to protect its surface. However anodizing process shall cause a lot waste water, and this water pollute environment.

Nowadays Aluminium flip tear off seal vial cap is normally use 8011 H16/H14 to make it, lacquered by epoxy clear varnish, or lacquered in different colors, normally in yellow color, golden color, red color, blue color and black color.

lacquered Aluminum strip Specification:

8011 H16/H14 Thickness 0.15–0.30mm, 宽度: 30mm —1000mm
内径: Paper core 76mm, 152mm and 80mm without core.
外径: 1200毫米, normally OD: 500–800mm.
包装: Wooden case, wooden pallet if request.

lacquered Aluminum strip Coating : 1. Both sides clear epoxy varnish 2. One side clear epoxy varnish, the other side color coated.

lacquered Aluminum strip Coating thickness :
Golden color /yellow color: both sides coating 5-6g/m2, one side coating 2-3g/m2.
White/red/black/blue color: Both sides coating 10-13g/m2.

lacquered Aluminum strip Coating quality :
1.Boiling Resistant: Boiling 121 degrees for half an hour, the paint does not fall off, do not change color.
2.Resistance to acetone and mercuric chloride: repeatedly wiping 20 times without significant stripping